| Brand | GMML-5A | GMML-10D | GMML-12 | GMML-9 | GMML-15 |
| MgO（%） | 91 | 86.9 | 84.5 | 86.7 | 81 |
| Al2O3（%） | 5.5 | 10.4 | 12 | 9.5 | 15.5 |
| Fe2O3（%） | 0.8 | 0.71 | 0.72 | 0.9 | 0.8 |
| CaO（%） | 1.4 | 1.36 | 1.36 | 1.62 | 1.4 |
| SiO2（%） | 0.7 | 0.63 | 0.8 | 1.0 | 0.7 |
| AP（%） | 16.0 | 17.0 | 17.0 | 17.2 | 17.0 |
| D.B.（g/cm3） | 2.96 | 2.94 | 2.91 | 2.95 | 2.94 |
| C.C.S（MPa） | 55 | 65 | 55 | 45 | 50 |
| RUL（T0.6）（℃） | 1700 | 1700 | 1700 | 1700 | 1700 |
| TRS（1100℃ Water） | 10 | 13 | 12 | 8 | 12 |
The above properties are guaranteed values based on long-term production statistics. Guomei may make the modification upon the production request.
Made from high purity magnesia (low impurty,C/S≥2)and high-grademagnesia alumina spinel, so it gives excellent high temperature performanceand excellent resistance against chemical attack. Higher spinel contentimproves flexibility and thermal shock resistance. Therefore, it is suitable to beused in transition zones of cement rotary kiin. Cement kiins in Europe widely usealternative fuels which bring about severe chemical erosion, large hightemperature area, frequent temperature fluctuation, and frequent conversionbetween oxidizing and reducing atmosphere in the kiln and our magnesia alumina spinelbrick has achieved good perforance in the transition zone and buming zone.
PREV ：NO MORE
NEXT：NO MORE
ABOUT US
Liaoning Guomagnesium Refractory Materials Co., Ltd
Address: Yong'an Town, Dashiqiao, Yingkou City, Liaoning Province
Contact person: Manager Qiu 18740258555
Tel ：0417-5223388
Fax：0417-5233388